Interface - The Journal of Wheel/Rail Interaction

RAIL GRINDING

Successful Grinding: Starting with the Basics
(Part 1 of 2)
By Norman Hooper • January 2010

It behooves railways to periodically review tie, fastener and surfacing maintenance practices, particularly as they relate to the planning and quality of rail grinding procedures. The use of technology, enhanced inspections, regular grinding cycles and friction modification can improve rail surface quality.

The safety rationale and cost effectiveness of rail grinding programs have become well established over the past 25 years (1). Rail grinding can remove plastic deformation and rolling contact fatigue (RCF) cracks that limit the life of rail (see Figure 1). If defects can be mitigated through grinding or effective rail testing, rail can be worn almost to the web — substantially increasing its service life. Grinding can control corrugation and weld dipping. Smoothing welds reduces dynamic impacts that can reduce a weld’s service life. Grinding can also help manage the wheel/rail contact profiles and steering forces. This is important because improved steering reduces the forces that cause wear and RCF. When combined with a program of lubrication and/or friction modification, rail grinding can double the rail’s wear life (2).

It's a good thing that grinding provides these benefits because it's expensive — as much as $30,000 per day. The maintenance challenge is to ensure that the money is well spent, and that the program delivers the anticipated benefits.

Obtaining the best value from grinding starts with proper inspection and planning. Before beginning a grinding program, maintenance personnel must ensure that the track is in reasonable condition. Grinding will not compensate for wide gauge, or correct tipped rail. In fact, profile grinding tipped rail can cause serious steering problems if the rail is re-set to the proper cant without an immediate re-grind. Grinding also will not improve the ride quality, if the track has poor crosslevel or alignment.

Consider a few “truths” about track:

• Every type of tie/fastening system wears out; all tie/fastening systems need maintenance over their service life.

• The level of deterioration is directly related to the loading over time.

• The rate of deterioration is exponential. Poor track deteriorates more quickly.

• The lowest lifecycle cost is achieved by timely preventive maintenance. Waiting too long to perform maintenance results in high expenditures for minimal benefits.

Deterioration of Tie/Fastening Systems

When inspecting track before a grinding program, the inspector must expect that the tie/fastening support systems will be in different stages of wear, and that some of them will be worn out. Not unexpectedly, rail surface conditions can be at their worst where the underlying tie support has deteriorated. Figures 2 - 6 show examples of deterioration that are found in typical tie/fastening systems.

The result of a failing tie/fastening system is wide gauge. Before the cause of wide gauge can be corrected, maintenance personnel have to understand and identify the mechanisms that cause it. These include a combination of:

• Rail tipping or rotation, resulting from plate cutting / tie failure (see Figure 2)

• Rail tipping or rotation, resulting from rail seat abrasion (see Figure 3)

• Plate movement / cutting due to insufficient anchors (see Figure 4)

• Longitudinal rail movement / failed anchors (see Figure 5)

• Lateral movement caused by worn tie plates, failed spikes/fasteners or worn pads (see Figure 6)

• Elongation of the spike holes

• Rail gauge-face wear (see Figure 7 on next page)

These mechanisms need to be treated differently when correcting gauge and when planning rail grinding programs. If, for example, the gauge is wide primarily because the rail is tipped to the field side, it is difficult to grind the rail for RCF down the center of the head. If the rail is subsequently reset to the proper cant, the profile contact patch will be off-center, seriously affecting steering. Tipped or improperly canted rails need to be reset before grinding.

This situation differs from one in which the high rail must be replaced because of gauge-face wear. The low rail, which typically shows signs of false flange contact at the field side of the rail head, must be ground for profile and RCF. In this instance, the existing track would not be re-gauged, as it would be too tight once the high rail is replaced. Track inspection and assessment of the factors contributing to wide gauge are essential to planning an effective rail grinding plan.

PAGE 1 OF 2 | NEXT PAGE >